Manufacturer: Jotun Paints
Jotun Penguard Express MIO is a two component amine cured epoxy coating. It is a fast drying, micaceous iron oxide (MIO) pigmented, high solids, high build product. Specially designed for new construction where fast dry to handle and over coating times are required.
Can be used as primer, mid coat, finish coat or as single coat system in atmospheric environments. Suitable for properly prepared carbon steel, stainless steel, aluminium and concrete substrates. It can be applied at sub zero surface temperatures.
- Fast drying
- Micaceous iron oxide (MIO) pigmented
- High solids, high build product
- It can be applied at sub zero surface temperatures
|Application Method ||Airless Spray or Brush |
|Surfaces ||Structural Steel / Offshore Environments / Buildings |
|VOC Levels ||278g / Litre |
|Coverage ||3m² / Litre |
|Touch Dry ||2 Hours @ 10°C / 30 Minutes @ 40°C |
|Over-Coating ||4 Hours @ 10°C / 1 Hour @ 40°C |
|Pot life @ 23°C ||2 Hours |
|Maintenance Cycle ||2 Years |
|Thinning & Cleaning ||Jotun No.17 |
|Number of Coats ||2 |
Surface Preparation: All surfaces should be clean, dry and free from contamination. The surface should be assessed and treated in accordance with ISO 8504.
Bare steel: Blast cleaning to Sa 21⁄2 (ISO 8501-1:1988). Roughness: using abrasives suitable to achieve grade Fine to Medium G (30-85 μm, Ry5) (ISO 8503-2).
Other surfaces: The coating may be used on other substrates.
Please contact us for more information.
Typical Use: Suitable for structural steel and piping to be exposed to highly corrosive environments, C5I or C5M (ISO 12944-2). Recommended for offshore environments, refineries, power plants, bridges, buildings and mining equipment.
Spray: Use airless spray.
Brush: Recommended for stripe coating and small areas. Care must be taken to achieve the specified dry film thickness.