Manufacturer: Jotun Paints
Penguard HSP is a two pack, amine cured, anticorrosive epoxy coating which is designed to speed up the paint schedule in the production. The ZP version contains extra Zinc Phosphate pigments to improve the anti-corrosive properties. It can be used as a primer, mid coat and finish coat or as a single coat system in urban and industrial atmospheres, coastal areas with low/moderate salinity.
- Fast drying
- High solids, high build product
- Very good water resistance
- Good flexibility
- Excellent solvent resistance
|Application Method ||Airless Spray and Brush |
|Mixing Ratio (Volume) ||Penguard HSP Comp A - 4 Parts |
|Penguard HSP Comp B - 1 Part |
|Surfaces ||Structural Steel / Buildings |
|VOC Level ||270g / Litre |
|Coverage ||3m² / Litre |
|Touch Dry || 5 Hours @ 5°C / 30 Minutes @ 40°C |
|Over-Coating ||12 Hours @ 5°C / 1 Hour @ 40°C |
|Maintenance Cycle ||2 Years @ 23°C |
|Pot life @ 23°C ||2 Hours |
|Thinning & Cleaning ||Jotun No.17 |
|Number of Coats ||2 |
Surface Preparation: To secure lasting adhesion to the subsequent product all surfaces shall be clean, dry and free from any contamination.
Carbon Steel: Minimum - St 2 (ISO 8501-1) Recommended - Sa 2½ (ISO 8501-1)
Coated surfaces: Minimum - Clean, dry and undamaged compatible coating (ISO 12944-5 6.1) Recommended - Clean, dry and undamaged compatible coating (ISO 12944-5 6.1)
Typical Paint System: Penguard HSP 2 x 75 μm (DFT) followed by Hardtop AS 1 x 60 μm (DFT)
Other systems may be specified, depending on area of use.
Typical Use: Suitable for properly prepared aluminium, carbon steel, galvanised steel, shop primed steel and stainless steel substrate. For structural steel and piping to be exposed to a range of corrosive environments. Recommended for power plants, airports, buildings, refineries and mining equipment.
Brush: Recommended for stripe coating and small areas. Care must be taken to achieve the specified dry film thickness.