Rust-Oleum 9200 Rust-O-Thane is a water Based, Polyurethane topcoat. It provides excellent protection against UV, with an easy to clean semi-gloss finish.
- Outstanding colour and gloss retention
- Very low VOC
- Resistant to solvents and chemical cleaning agents
- High resistance to abrasion
- Long-lasting satin finish
- Also suitable for floors or walls
|Application Method ||Spray, Brush or Roller |
|Surfaces ||Coated floors, walls and primed metal |
|VOC level ||35g / Litre |
|Coverage ||6.2m² / Litre |
|Touch Dry ||1 Hour 30 Minutes - 2 Hours @ 20°C |
|Over-Coating ||24 Hours @ 20°C |
|Maintenance Cycle ||2 Years |
|Thinning & Cleaning ||Water & Soap |
|Number of Coats ||2 |
Surface Preparation: Remove grease, oil and all other surface contamination using alkaline or high pressure (steam) cleaning in combination with appropriate detergents. Sand previous coatings that are in good condition to remove gloss and to roughen the surface slightly. Assure that the previous coating is compatible with the RUST-O-THANE 9200 by making a test application! Remove bad adhering coatings by scraping, wire brushing or sanding. (Spot)prime with commended Rust-Oleum or Mathys coatings. The surface must be clean and dry during application.
Typical Paint System
Suitable Primer to manufactures recommendation
9200 1 x 40µm (Dry Film Thickness)
Typical Use: For application on substrates, which are coated with Rust-oleum or Martin Mathys epoxy or acrylic coatings. The application areas consist of coated floors, coated walls, and primed metal.
Application: Temperature of air, substrate and coating material between 5°C and 35°C and relative humidity below 80 %. The substrate temperature must be at least 3°C above dew point.
Brush: Undiluted. Use natural bristles, longhair brushes.
Roller: Undiluted. Use medium nap (polyamide, 8-12 mm). Apply slowly in even strokes.
Airless spray: Undiluted. Pneumatic and electric airless equipment. Tip size: 0.013-0.015 inch. Fluid pressure: 200 bar.
Cleanup: Water and soap, before drying.